Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique
The analysis of x-ray diffraction (XRD) patterns by the Rietveld technique was tested to the quantitatively phase compositions of self reinforcement Al2O3/CaAl12O19 composite. Room-temperature XRD patterns revealed that a-Al2O3 was the only phase presence in the CA0 sample, whereas the a-Al 2O3 and...
| Main Authors: | , , |
|---|---|
| Format: | Conference Paper |
| Published: |
2008
|
| Online Access: | http://hdl.handle.net/20.500.11937/43178 |
| _version_ | 1848756618863312896 |
|---|---|
| author | Asmi, D. Low, It Meng O'Connor, B. |
| author_facet | Asmi, D. Low, It Meng O'Connor, B. |
| author_sort | Asmi, D. |
| building | Curtin Institutional Repository |
| collection | Online Access |
| description | The analysis of x-ray diffraction (XRD) patterns by the Rietveld technique was tested to the quantitatively phase compositions of self reinforcement Al2O3/CaAl12O19 composite. Room-temperature XRD patterns revealed that a-Al2O3 was the only phase presence in the CA0 sample, whereas the a-Al 2O3 and CaAl12O19 phases were found for CA5, CA15, CA30, and CA50 samples. The peak intensity of CA6 in the self reinforcement Al2O3/CaAl12O 19 composites increased in proportion with increase in CaAl 12O19 content in contrast to a-Al2O 3. The diffraction patterns for CA100 sample shows minor traces of a-Al2O3 even in relatively low peak intensity. It is suggesting that the in-situ reaction sintering of raw materials were not react completely to form 100 wt% CaAl12O19 at temperature 1650°C. Quantitative phase compositions of self reinforcement Al 2O3/CaAl12O19 composites by Rietveld analysis with XRD data has been well demonstrated. The results showed that the GOF values are relatively low and the fluctuation in the difference plots shows a reasonable fit between the observed and the calculated plot. © 2008 American Institute of Physics. |
| first_indexed | 2025-11-14T09:15:04Z |
| format | Conference Paper |
| id | curtin-20.500.11937-43178 |
| institution | Curtin University Malaysia |
| institution_category | Local University |
| last_indexed | 2025-11-14T09:15:04Z |
| publishDate | 2008 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | curtin-20.500.11937-431782023-08-02T06:39:08Z Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique Asmi, D. Low, It Meng O'Connor, B. The analysis of x-ray diffraction (XRD) patterns by the Rietveld technique was tested to the quantitatively phase compositions of self reinforcement Al2O3/CaAl12O19 composite. Room-temperature XRD patterns revealed that a-Al2O3 was the only phase presence in the CA0 sample, whereas the a-Al 2O3 and CaAl12O19 phases were found for CA5, CA15, CA30, and CA50 samples. The peak intensity of CA6 in the self reinforcement Al2O3/CaAl12O 19 composites increased in proportion with increase in CaAl 12O19 content in contrast to a-Al2O 3. The diffraction patterns for CA100 sample shows minor traces of a-Al2O3 even in relatively low peak intensity. It is suggesting that the in-situ reaction sintering of raw materials were not react completely to form 100 wt% CaAl12O19 at temperature 1650°C. Quantitative phase compositions of self reinforcement Al 2O3/CaAl12O19 composites by Rietveld analysis with XRD data has been well demonstrated. The results showed that the GOF values are relatively low and the fluctuation in the difference plots shows a reasonable fit between the observed and the calculated plot. © 2008 American Institute of Physics. 2008 Conference Paper http://hdl.handle.net/20.500.11937/43178 10.1063/1.2906057 restricted |
| spellingShingle | Asmi, D. Low, It Meng O'Connor, B. Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique |
| title | Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique |
| title_full | Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique |
| title_fullStr | Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique |
| title_full_unstemmed | Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique |
| title_short | Phase compositions of self reinforcement Al2O 3/CaAl12O19 composite using X-ray diffraction data and rietveld technique |
| title_sort | phase compositions of self reinforcement al2o 3/caal12o19 composite using x-ray diffraction data and rietveld technique |
| url | http://hdl.handle.net/20.500.11937/43178 |