Highly ordered 3D macroporous scaffold supported Pt/C oxygen electrodes with superior gas-proton transportation properties and activities for fuel cells
© The Royal Society of Chemistry 2015. An oxygen electrode finds many applications in various electrochemical energy conversion devices such as fuel cells and metal-air batteries. Highly efficient gas-proton transportation at the electrode is very important to enhance the power density of these devi...
| Main Authors: | , , , , , , |
|---|---|
| Format: | Journal Article |
| Published: |
2015
|
| Online Access: | http://purl.org/au-research/grants/arc/DP120104932 http://hdl.handle.net/20.500.11937/40222 |
| Summary: | © The Royal Society of Chemistry 2015. An oxygen electrode finds many applications in various electrochemical energy conversion devices such as fuel cells and metal-air batteries. Highly efficient gas-proton transportation at the electrode is very important to enhance the power density of these devices. Herein, we report the construction of a highly efficient oxygen electrode with substantially improved proton conductivity and gas transportation properties using three dimensionally ordered macroporous Nafion/Cs2.5H0.5PW12O40, 3DOM Nafion/CsHPW, scaffold supported Pt/C nanocomposites. The best results were obtained for cells with 3DOM Nafion/CsHPW with 10% CsHPW, achieving a maximum power density of 955 mW cm-2, 31% higher than 730 mW cm-2 for the cell with the conventional Nafion-binder based oxygen electrode. The proton conductivity of the 10% 3DOM Nafion/CsHPW catalyst layer is 1.56 × 10-2 S cm-1, 112% higher than 7.35 × 10-3 S cm-1 measured for the conventional catalyst layer with the Nafion binder. The results demonstrate the significant advantages of the oxygen electrodes with the Pt/C-3DOM Nafion/CsHPW architecture over the conventional Nafion-binder based ones, with the significantly enhanced proton conductivity of uniformly distributed CsHPW nanoparticles (NPs) and much better gas diffusion properties of the 3DOM architecture. |
|---|