Anti-corrosion behaviour of VE/GF coatings on mild steel
In this study, the properties of vinyl ester/glass flake (VE/GF) coating on mild steel plates was investigated to determine its anti-corrosion performance. The corrosion penetration rate of VE/GF coated and uncoated mild steel was evaluated using immersion tests for 20 days. Corrosion resistance of...
| Main Authors: | , , |
|---|---|
| Format: | Journal Article |
| Published: |
Carl Hanser Verlag
2014
|
| Subjects: | |
| Online Access: | http://hdl.handle.net/20.500.11937/3570 |
| _version_ | 1848744267684511744 |
|---|---|
| author | Barbhuiya, Salim Choudhury, I. Memon, S. |
| author_facet | Barbhuiya, Salim Choudhury, I. Memon, S. |
| author_sort | Barbhuiya, Salim |
| building | Curtin Institutional Repository |
| collection | Online Access |
| description | In this study, the properties of vinyl ester/glass flake (VE/GF) coating on mild steel plates was investigated to determine its anti-corrosion performance. The corrosion penetration rate of VE/GF coated and uncoated mild steel was evaluated using immersion tests for 20 days. Corrosion resistance of the coating was evaluated in various corrosive environments viz. 5% HCl, 8% HCl, 5% NaOH and 7% NaOH. The mild steel plates were coated with four different thicknesses of VE/GF coating and a comparative analysis was carried out to evaluate the corrosion protection efficiency. Scanning electron microscopy was carried out before and after the immersion test to study the morphological changes and products of corrosion. |
| first_indexed | 2025-11-14T05:58:45Z |
| format | Journal Article |
| id | curtin-20.500.11937-3570 |
| institution | Curtin University Malaysia |
| institution_category | Local University |
| last_indexed | 2025-11-14T05:58:45Z |
| publishDate | 2014 |
| publisher | Carl Hanser Verlag |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | curtin-20.500.11937-35702017-09-13T14:45:49Z Anti-corrosion behaviour of VE/GF coatings on mild steel Barbhuiya, Salim Choudhury, I. Memon, S. Vinyl ester/glass flake Immersion test Anti-corrosion performance Coatings In this study, the properties of vinyl ester/glass flake (VE/GF) coating on mild steel plates was investigated to determine its anti-corrosion performance. The corrosion penetration rate of VE/GF coated and uncoated mild steel was evaluated using immersion tests for 20 days. Corrosion resistance of the coating was evaluated in various corrosive environments viz. 5% HCl, 8% HCl, 5% NaOH and 7% NaOH. The mild steel plates were coated with four different thicknesses of VE/GF coating and a comparative analysis was carried out to evaluate the corrosion protection efficiency. Scanning electron microscopy was carried out before and after the immersion test to study the morphological changes and products of corrosion. 2014 Journal Article http://hdl.handle.net/20.500.11937/3570 10.3139/146.111133 Carl Hanser Verlag restricted |
| spellingShingle | Vinyl ester/glass flake Immersion test Anti-corrosion performance Coatings Barbhuiya, Salim Choudhury, I. Memon, S. Anti-corrosion behaviour of VE/GF coatings on mild steel |
| title | Anti-corrosion behaviour of VE/GF coatings on mild steel |
| title_full | Anti-corrosion behaviour of VE/GF coatings on mild steel |
| title_fullStr | Anti-corrosion behaviour of VE/GF coatings on mild steel |
| title_full_unstemmed | Anti-corrosion behaviour of VE/GF coatings on mild steel |
| title_short | Anti-corrosion behaviour of VE/GF coatings on mild steel |
| title_sort | anti-corrosion behaviour of ve/gf coatings on mild steel |
| topic | Vinyl ester/glass flake Immersion test Anti-corrosion performance Coatings |
| url | http://hdl.handle.net/20.500.11937/3570 |