Mix design and production of flyash based geopolymer concrete
Geopolymer is a new development in the world of concrete in which cement is totally replaced by pozzolanic materials like fly ash and activated by highly alkaline solutions to act as a binder in the concrete mix. For the selection of suitable ingredients of geopolymer concrete to achieve desire stre...
| Main Author: | |
|---|---|
| Format: | Journal Article |
| Published: |
The Associated Cement Companies Limited
2008
|
| Online Access: | http://hdl.handle.net/20.500.11937/25939 |
| _version_ | 1848751845119361024 |
|---|---|
| author | Rangan, B. Vijaya |
| author_facet | Rangan, B. Vijaya |
| author_sort | Rangan, B. Vijaya |
| building | Curtin Institutional Repository |
| collection | Online Access |
| description | Geopolymer is a new development in the world of concrete in which cement is totally replaced by pozzolanic materials like fly ash and activated by highly alkaline solutions to act as a binder in the concrete mix. For the selection of suitable ingredients of geopolymer concrete to achieve desire strength at required workability, an experimental investigation has been carried out for the gradation of geopolymer concrete and a mix design procedure is proposed on the basis of quantity and fineness of fly ash, quantity of water, grading of fine aggregate, fine to total aggregate ratio. Sodium silicate solution with Na2O = 16.37 %, SiO2 = 34.35 % and H2O = 49.28 % and sodium hydroxide solution having 13 M concentration were maintained constant throughout the experiment. Water-to-geopolymer binder ratio of 0.35, alkaline solution-to-fly ash ratio of 0.35 and sodium silicate-to-sodium hydroxide ratio of 1.0 by mass were fixed on the basis of workability and cube compressive strength. Workability of geopolymer concrete was measured by flow table apparatus and cubes of 150 mm side were cast and tested for compressive strength after specified period of oven heating. The temperature of oven heating was maintained at 60 °C for 24 h duration and tested 7 days after heating. It is observed that the results of workability and compressive strength are well match with the required degree of workability and compressive strength. So, proposed method is used to design normal and standard geopolymer concrete. |
| first_indexed | 2025-11-14T07:59:12Z |
| format | Journal Article |
| id | curtin-20.500.11937-25939 |
| institution | Curtin University Malaysia |
| institution_category | Local University |
| last_indexed | 2025-11-14T07:59:12Z |
| publishDate | 2008 |
| publisher | The Associated Cement Companies Limited |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | curtin-20.500.11937-259392017-09-13T15:24:21Z Mix design and production of flyash based geopolymer concrete Rangan, B. Vijaya Geopolymer is a new development in the world of concrete in which cement is totally replaced by pozzolanic materials like fly ash and activated by highly alkaline solutions to act as a binder in the concrete mix. For the selection of suitable ingredients of geopolymer concrete to achieve desire strength at required workability, an experimental investigation has been carried out for the gradation of geopolymer concrete and a mix design procedure is proposed on the basis of quantity and fineness of fly ash, quantity of water, grading of fine aggregate, fine to total aggregate ratio. Sodium silicate solution with Na2O = 16.37 %, SiO2 = 34.35 % and H2O = 49.28 % and sodium hydroxide solution having 13 M concentration were maintained constant throughout the experiment. Water-to-geopolymer binder ratio of 0.35, alkaline solution-to-fly ash ratio of 0.35 and sodium silicate-to-sodium hydroxide ratio of 1.0 by mass were fixed on the basis of workability and cube compressive strength. Workability of geopolymer concrete was measured by flow table apparatus and cubes of 150 mm side were cast and tested for compressive strength after specified period of oven heating. The temperature of oven heating was maintained at 60 °C for 24 h duration and tested 7 days after heating. It is observed that the results of workability and compressive strength are well match with the required degree of workability and compressive strength. So, proposed method is used to design normal and standard geopolymer concrete. 2008 Journal Article http://hdl.handle.net/20.500.11937/25939 10.1007/978-81-322-2187-6_123 The Associated Cement Companies Limited restricted |
| spellingShingle | Rangan, B. Vijaya Mix design and production of flyash based geopolymer concrete |
| title | Mix design and production of flyash based geopolymer concrete |
| title_full | Mix design and production of flyash based geopolymer concrete |
| title_fullStr | Mix design and production of flyash based geopolymer concrete |
| title_full_unstemmed | Mix design and production of flyash based geopolymer concrete |
| title_short | Mix design and production of flyash based geopolymer concrete |
| title_sort | mix design and production of flyash based geopolymer concrete |
| url | http://hdl.handle.net/20.500.11937/25939 |