Intergranular stress corrosion cracking of 13Cr weldable martensitic stainless steels

QR Code

Intergranular stress corrosion cracking of 13Cr weldable martensitic stainless steels

Weldable martensitic stainless steels (13Cr) used in the oil and gas industry can suffer from intergranular stress corrosion cracking (IGSCC). In this study, sensitisation in the heat-affected zone of welds that can cause intergranular attack and IGSCC under service conditions was characterised. By...

Full description

Bibliographic Details
Main Author:	Maier, Jens
Format:	Thesis
Language:	English
Published:	Curtin University 2012
Online Access:	http://hdl.handle.net/20.500.11937/1633

Similar Items

Local electrochemistry and scanning probe microscopy techniques to clarify intergranular cracking phenomena in weldable martensitic stainless steels
by: Maier, J., et al.
Published: (2009)

Sensitisation identification of stainless steel to intergranular stress corrosion cracking by atomic force microscopy
by: Yanliang, Huang, et al.
Published: (2008)

Weldability of duplex stainless steel
by: Pramanik, Alokesh, et al.
Published: (2015)

Weldability and machinability of duplex stainless steel
by: Pramanik, Alokesh, et al.
Published: (2015)

Investigation of chloride stress corrosion cracking in austenitic stainless steel
by: Mohamad Khairuazlan, Kamaruzaman
Published: (2013)

3D Atom-Probe Characterization of Stress and Cold-Work in Stress Corrosion Cracking of 304 Stainless Steel
by: Kruska, K., et al.
Published: (2011)

Dry turning of tempered martensitic stainless tool steel using coated cermet and coated carbide tools.
by: Noordin, M. Y., et al.
Published: (2007)

Influences of H2SO4 and NaCl Concentrations on Stress Corrosion Cracking of AISI 304 Stainless Steel
by: Nur Azhani, Abd Razak, et al.
Published: (2014)

Stress Corrosion Cracking of Stainless Steel 316L Additively Manufactured using Sinter-based and Laser-based Technologies
by: Santamaria Torres, Ricardo Andres
Published: (2023)

Effect of composition and microstructure on hydrogen embrittlement resistance — Ferritic/martensitic and bainitic/martensitic low alloy steels
by: Rodoni, Esteban
Published: (2023)

MIC and Cracking of Mild and Stainless Steels
by: Javaherdashti, Reza
Published: (2010)

Effect of Tungsten on the Pitting and Crevice Corrosion Resistance of Type 25Cr Super Duplex Stainless Steels
by: Iannuzzi, Mariano, et al.
Published: (2016)

The effect of temperature on the chromizing process for Ferritic-Martensitic steel
by: F, Farah Alia, et al.
Published: (2017)

Corrosion at Sulphide Inclusions in Stainless Steel
by: Daud, A. R.
Published: (1996)

Effect of Ferritic - Martensitic Constituent on Mechanical Property and Corrosion Behaviour of Medium Carbon Dual Phase (DP) Steel
by: Radhiyah, Abd Aziz, et al.
Published: (2018)

Effect Of Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Low Carbon Steel Using Martensite Starting Microstructure
by: Ahmad, Muhammad Syafiq
Published: (2020)

Hydrogen-induced stress cracking of swaged super duplex stainless steel subsea components
by: Hazarabedian, M.S., et al.
Published: (2019)

Effect of Cracking on Corrosion of Steel in Concrete
by: Shaikh, Faiz
Published: (2018)

Corrosion of Stainless Steels in the Marine Splash Zone
by: Bailey, Stuart, et al.
Published: (2013)

The Role of Tungsten on the Phase Transformation Kinetics and its Correlation with the Localized Corrosion Resistance of 25Cr Super Duplex Stainless Steels.
by: Torres, Cristian, et al.
Published: (2020)

Comparison of erosion corrosion of titanium and stainless steel in seawater
by: Mohamad Izwan, Abdul Ghani
Published: (2012)

Corrosion behavior of duplex stainless steel in sea water
by: -, Suryanto
Published: (2011)

Morphological evolution studies of pitting corrosion of Stainless Steel
by: Gualteros Vanegas, Mayra Liliana
Published: (2024)

Study the effect of martensite-ferrite comstituents phase of the plain medium carbon dual phase (DP) steel on the mechanical property and corrosion behavior
by: Maisalsadila, Ismail
Published: (2017)

Study of pitting corrosion on mild steel and stainless steel by electrochemical noise technique
by: Hashim, I. H., et al.
Published: (2009)

The effect of torch distance on weldability of dissimilar welding
by: Ashaari, Ibrahim
Published: (2013)

The effects of particle angularity on low-stress three-body abrasion-corrosion of 316L stainless steel
by: Stachowiak, Grazyna, et al.
Published: (2016)

Investigation of corrosion effects on aluminum-stainless steel weld joint
by: Nurul Asmida, Kamaruddin
Published: (2012)

Study of geometric effect to the crevice corrosion behaviour in stainless steel
by: Neena Kaylisia, Brum
Published: (2013)

Microbial Corrosion Resistance of Stainless Steels for Marine Energy Installations
by: Machuca, L., et al.
Published: (2011)

Fatigue crack growth analysis of stainless steel under mode 1
by: Ahmad Azam Azizan, Azlan
Published: (2010)

Experimental Analysis on Martensite Formation of Low Carbon Steel During Rapid Cooling Process
by: Mohd Zaidi, Sidek, et al.
Published: (2013)

Hydrogen induced stress cracking of super duplex stainless steel UNS S32760 - A root cause failure investigation
by: Hazarabedian, M.S., et al.
Published: (2019)

Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s
by: Asmara, Y. P., et al.
Published: (2013)

Mechanistic model of stress corrosion cracking (scc) of carbon steel in acidic solution with the presence of H2s
by: Asmara, Y. P., et al.
Published: (2013)

Influence of tungsten on passivity breakdown and repassivation of 25CR super duplex stainless steel
by: Torres, C., et al.
Published: (2018)

Characterisation of weldability and metallurgical stability of dissimilar metal welds
by: Bin Azahari, Ahmad Azli
Published: (2020)

Effect of clamping distance and voltage on weldability of dissimilar welding
by: Veyolla, Jaffrey
Published: (2013)

Crevice corrosion of duplex stainless steels in the presence of natural marine biofilms
by: Machuca, Laura, et al.
Published: (2012)

Damage mechanics based predictions of creep crack growth in 316 stainless steel
by: Hyde, Christopher J., et al.
Published: (2010)

Cannot write session to /tmp/vufind_sessions/sess_iu6tqj10ra96v69q69ujshb184